PEAK CONCRETE RELEASE AGENT B4
CONCRETE FORM & MOULD OIL
PRODUCT DESCRIPTION
PEAK CONCRETE RELEASE AGENT B4 is a release agent used in the process of manufacturing concrete slabs and pre-stressed concrete. It is specially formulated with a vegetable-based ester and light mineral oil to ensure clean release from steel, aluminium, plywood or composite forms, ensuring a high-quality concrete surface finish. It is also designed for use in enclosed environments where a low odour and environmentally sensitive product is desired.
NOTE: If the reinforcing steel is accidentally coated with mould oil, the steel may not bond to the concrete. Mould oil on the reinforcing steel should be removed with kerosene or other similar solvents.
BENEFITS
- Excellent surface conditioning characteristics
- Formulated to deliver clean concrete release
- Low odour and environmentally friendly
APPLICATION
- Applied by mop, roller, brush or spray. The application temperature should be above 5°C as product may become cloudy at lower temperatures.
- Roller Method: The oil is used for coating the walls and floors of rectangular moulds before pouring aerated concrete. Forms and moulds should be clean and reasonably dry for each pour and should be coated before the reinforcing steel is put in place.
- Spray Method: Recommended for large-scale production. It is desirable that a light coating be applied to avoid excess to run off which can permeate the concrete. The spray lines must be regularly blown out and it is recommended that moisture traps be placed in the lines. Apply at a rate of 10 – 20ml/m2.
CHARACTERISTICS
| Test | Typical Value |
|---|---|
| Density 15°C g/cm³ | 0.875 |
| Viscosity @ 40°C cSt | 7.3 |
| Viscosity @ 100°C cSt | 2.4 |
| Flash Point °C | >150 |
PRODUCT SIZE
| Part Number | Size | Carton Qty | Pallet Qty |
|---|---|---|---|
| PKICRA020 | 20 Litre | 32 | |
| PKICRA205 | 205 Litre | 4 |